Υγρός αφρός ρητίνης πολυουρεθάνης για την κατασκευή σόλας
Λάβετε την τελευταία τιμήΤρόπος Πληρωμής: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Παραγγελία: | 1000 Kilogram |
μεταφορά: | Ocean,Land,Air |
Λιμάνι: | Shanghai |
Τρόπος Πληρωμής: | L/C,T/T |
Incoterm: | FOB,CIF |
Min. Παραγγελία: | 1000 Kilogram |
μεταφορά: | Ocean,Land,Air |
Λιμάνι: | Shanghai |
Αρ. μοντέλου: XC-9080W,XC-6088
Μάρκα: Χημική ουσία Xuchuan
τόπο καταγωγής: Κίνα
Τύποι: Συνθετική ρητίνη και πλαστικά
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line
Appearance: Liquid
Application: shoe sole
Keywords: liquid polyurethane resin,insole material memory foam,insole foam
Ισοκυανικό πολυόλης για τα μέσα της σόλας
Application | shoe sole |
Keywords | liquid polyurethane resin,insole material memory foam,insole foam |
A/B Materials Temperatures(℃) | A/B Materials Temperatures(℃) |
A+C/B Mix ratio (By weight) | 100/100~102 |
Cream Time (s) | 6~8 |
End of Rise Time (s) | 30~40 |
Free Rise Foam Density(g/cm3) | 0.21~0.26 |
Mold Temperature(℃) | 45~55 |
Demold Time(min) | Demold Time(min) |
Molded Density (g/cm3) | 0.35~0.60 |
Characteristic: Low density and high hardness, good appearance, little pinhole, and weak foam line |
|||||||
Application: Outsole, slippers, wedge shoes |
|||||||
Typical properties of PU matrix |
|||||||
Name of products |
Appearance |
Viscosity (mPa·s/40℃) |
Density (g·cm-3/40℃) |
Package(kg) |
/ |
/ |
/ |
A-9080W |
Cream,White,liquid |
1000~1300 |
1.01~1.02 |
18 |
/ |
/ |
/ |
B-6088 |
Yellowish transparent liquid or waxy |
600~800 |
1.08~1.2 |
20 |
/ |
/ |
/ |
Materials preheat |
|||||||
A-9080W: preheated at 50~60℃ for 6~8 hours. |
|||||||
B-6088: preheated at 50~60℃ for 6~8 hours. |
|||||||
Typical processing parameters & Reaction parameter. |
|||||||
Items |
A/B Materials Temperatures(℃) |
A+C/B Mix ratio |
Cream Time (s) |
End of Rise Time (s) |
Free Rise Foam Density(g/cm3) |
Mold Temperature(℃) |
Demold Time(min) |
Parameter |
40~45/38~42 |
100/100~102 |
6~8 |
30~40 |
0.21~0.26 |
45~55 |
5~7 |
The adding content of C-2 should be 210g±10g/18kg. |
|||||||
The adding content of water should be 0~80g/18kg according to the reality. |
|||||||
The adding content of hardener should be 0~1200g/18kg according to the reality. |
|||||||
Physical properties |
|||||||
Items |
Molded Density (g/cm3) |
Hardness |
Tensile strength |
Elongation |
Tear Strength |
Williams abrasion |
/ |
Physical properties |
0.35~0.60 |
60~88 |
4~7 |
200~300 |
11~20 |
130~200 |
/ |
Demold time may be prolonged with the increase of sole thickness. |
|||||||
These physical data are acquired by testing a sample of 6mm thick. |
|||||||
Data listed above are just for reference. The detail data are subjected to practical production. If other requests for physical properties, please contact us. |
Η Xuchuan Chemical που ιδρύθηκε το 2007, η Εταιρεία Εγγεγραμμένη Capital είναι 500 εκατομμύρια RMB. Τα κύρια προϊόντα είναι όλα τα πολυεστέρα πολυολικό πολυολικό πολυολικό, πολυουρεθάνη ρητίνη για παπούτσια, ρητίνες πολυουρεθάνης χωρίς νερό και χωρίς διαλύτη για τεχνητά δερμάτινα δερμάτινα, συγκολλητικά συγκόλλησης πολυουρεθάνης και συγκολλητικά ζεστά τήγμα πολυουρεθάνης.
Τώρα το Xuchuan έχει 4 σύγχρονες βάσεις παραγωγής, η παραγωγική ικανότητα έφτασε στους 630.000 τόνους ετησίως, τα προϊόντα που εξάγονται σε 32 χώρες και περιοχές στον κόσμο.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.